1.1 This part of GB/T 8323 specifies a method of measuring smoke production from the exposed surface of specimens of essentially flat materials, composites or assemblies not exceeding 25 mm in thickness when placed in a horizontal orientation and subjected to specified levels of thermal irradiance in a closed cabinet with or without the application of a pilot flame. This method of test is applicable to all plastics and may also be used for the evaluation of other materials (e.g. rubbers, textile-coverings, painted surfaces, wood and other materials).
1.2 It is intended that the values of optical density determined by this test be taken as specific to the specimen or assembly material in the form and thickness tested, and are not to be considered inherent, fundamental, properties.
1.3 The test is intended primarily for use in research and development and in fire safety engineering of buildings, trains, ships, etc., and not as a basis for ratings for building codes or other purposes. No basis is provided for predicting the density of smoke that may be generated by the materials upon exposure to heat and flame under other (actual) exposure conditions, nor is any correlation established with measurements derived from other test methods. This test procedure excludes the effect of irritants on the eye.
NOTE: This test procedure addresses the loss of visibility due to smoke density, which generally is not related to irritancy potency, as explained in Part 1 of this International Standard.
1.4 It is emphasized that smoke production from a material varies according to the irradiance level to which the specimen is exposed. In making use of the results of this method, it should be borne in mind that the results are based on exposure to the specific irradiance levels of 25 kW/m2 and 50 kW/m2.
Contents
Foreword I
1 Scope
2 Normative References
3 Terms and Definitions
4 Principles of the Test
5 Suitability of a material for testing
6 Specimen construction and preparation
7 Apparatus and ancillary equipment
8 Test Environment
9 Setting-up and Calibration Procedures
10 Test Procedure
11 Expression of Results
12 Precision
13 Test report
Appendix A (Normative) Calibration of Heat Flux Meter
Appendix B (Informative) Variability in the Specific Optical Density of Smoke Measured in the Single-chamber Test
Appendix C (Informative) Determination of Mass Optical Density
Appendix D (Informative) Precision Data from Tests on Intumescent Materials
Bibliography
1.1 This part of GB/T 8323 specifies a method of measuring smoke production from the exposed surface of specimens of essentially flat materials, composites or assemblies not exceeding 25 mm in thickness when placed in a horizontal orientation and subjected to specified levels of thermal irradiance in a closed cabinet with or without the application of a pilot flame. This method of test is applicable to all plastics and may also be used for the evaluation of other materials (e.g. rubbers, textile-coverings, painted surfaces, wood and other materials).
1.2 It is intended that the values of optical density determined by this test be taken as specific to the specimen or assembly material in the form and thickness tested, and are not to be considered inherent, fundamental, properties.
1.3 The test is intended primarily for use in research and development and in fire safety engineering of buildings, trains, ships, etc., and not as a basis for ratings for building codes or other purposes. No basis is provided for predicting the density of smoke that may be generated by the materials upon exposure to heat and flame under other (actual) exposure conditions, nor is any correlation established with measurements derived from other test methods. This test procedure excludes the effect of irritants on the eye.
NOTE: This test procedure addresses the loss of visibility due to smoke density, which generally is not related to irritancy potency, as explained in Part 1 of this International Standard.
1.4 It is emphasized that smoke production from a material varies according to the irradiance level to which the specimen is exposed. In making use of the results of this method, it should be borne in mind that the results are based on exposure to the specific irradiance levels of 25 kW/m2 and 50 kW/m2.
Contents of GB/T 8323.2-2008
Contents
Foreword I
1 Scope
2 Normative References
3 Terms and Definitions
4 Principles of the Test
5 Suitability of a material for testing
6 Specimen construction and preparation
7 Apparatus and ancillary equipment
8 Test Environment
9 Setting-up and Calibration Procedures
10 Test Procedure
11 Expression of Results
12 Precision
13 Test report
Appendix A (Normative) Calibration of Heat Flux Meter
Appendix B (Informative) Variability in the Specific Optical Density of Smoke Measured in the Single-chamber Test
Appendix C (Informative) Determination of Mass Optical Density
Appendix D (Informative) Precision Data from Tests on Intumescent Materials
Bibliography